1. 直缝焊管生产工艺简单，生产效率高，成本低，发展较快。螺旋焊管的强度一般比直缝焊管高，能用较窄的坯料生产管径较大的焊管，还可以用同样宽度的坯料生产管径不同的焊管。但是与相同长度的直缝管相比，焊缝长度增加30~100%，而且生产速度较低。因此，较小口径的焊管大都采用直缝焊，大口径焊管则大多采用螺螺旋焊产品广泛应用于
|
公称外径 nominal O.D
mm |
公称壁厚 Nominal Wall Thickness mm |
|
5.0 |
5.5 |
6.0 |
7.0 |
8.0 |
9.0 |
10.0 |
11.0 |
12.0 |
13.0 |
14.0 |
15.0 |
16.0 |
18.0 |
20.0 |
22.0 |
|
219 |
26.39 |
28.96 |
31.51 |
36.60 |
41.63 |
|
|
|
|
|
|
|
|
|
|
|
|
273 |
33.04 |
36.28 |
39.51 |
45.92 |
|
|
|
|
|
|
|
|
|
|
|
|
|
325 |
39.46 |
43.33 |
47.26 |
54.90 |
62.54 |
70.13 |
|
|
|
|
|
|
|
|
|
|
|
377 |
45.88 |
50.39 |
54.89 |
63.87 |
72.80 |
81.67 |
|
|
|
|
|
|
|
|
|
|
|
426 |
51.91 |
57.03 |
62.14 |
72.33 |
82.46 |
92.55 |
102.59 |
|
|
|
|
|
|
|
|
|
|
457 |
55.73 |
61.24 |
66.73 |
77.69 |
88.58 |
99.43 |
110.23 |
120.98 |
131.60 |
142.34 |
|
|
|
|
|
|
|
508 |
|
|
74.28 |
86.48 |
98.64 |
110.75 |
122.81 |
134.82 |
146.78 |
158.69 |
|
|
|
|
|
|
|
529 |
|
|
77.38 |
90.11 |
102.78 |
115.41 |
127.99 |
140.51 |
152.99 |
165.42 |
|
|
|
|
|
|
无锡市洋利特钢管有限公司螺旋钢管生产工艺
螺旋钢管是以带钢卷板为原材料,经常温挤压成型,以自动双丝双面埋弧焊工艺焊接而成的螺旋缝钢管.
（1）原材料即带钢卷，焊丝，焊剂。在投入前都要经过严格的理化检验。
（2）带钢头尾对接，采用单丝或双丝埋弧焊接，在卷成钢管后采用自动埋弧焊补焊。
（3）成型前，带钢经过矫平、剪边、刨边，表面清理输送和予弯边处理。（4）采用电接点压力表控制输送机两边压下油缸的压力，确保了带钢的平稳输送。
（5）采用外控或内控辊式成型。
（6）采用焊缝间隙控制装置来保证焊缝间隙满足焊接要求，管径，错边量和焊缝间隙都得到严格的控制。
（7）内焊和外焊均采用美国林肯电焊机进行单丝或双丝埋弧焊接，从而获得稳定的焊接规范。
（8）焊完的焊缝均经过在线连续超声波自动伤仪检查，保证了100％的螺旋焊缝的无损检测覆盖率。若有缺陷，自动报警并喷涂标记，生产工人依此随时调整工艺参数，及时消除缺陷。
（9）采用空气等离子切割机将钢管切成单根。
（10）切成单根钢管后，每批钢管头三根要进行严格的首检制度，检查焊缝的力学性能，化学成份，溶合状况，钢管表面质量以及经过无损探伤检验，确保制管工艺合格后，才能正式投入生产。
（11）焊缝上有连续声波探伤标记的部位，经过手动超声波和X射线复查，如确有缺陷，经过修补后，再次经过无损检验，直到确认缺陷已经消除。
（12）带钢对焊焊缝及与螺旋焊缝相交的丁型接头的所在管，全部经过X射线电视或拍片检查。
（13）每根钢管经过静水压试验，压力采用径向密封。试验压力和时间都由钢管水压微机检测装置严格控制。试验参数自动打印记录。
（14）管端机械加工，使端面垂直度，坡口角和钝边得到准确控制。 |